Descrizione
Caratteristiche:
LKE-9016-B91 is a low hydrogen electrode. The weld metal contains 9%Cr-1%Mo and some little Nb,V to improve the creep problem at prolonged high temperature. With stable arc, low spatter and easy slag removal.
Applicazioni:
It is suitable for welding of the steel such as ASTM A213-T91, A335 P91, A387 Gr.91,A182 F91.
Note sull'uso:
1.Dry the electrodes at 350-400°C for 60 minutes before use.
2.Do not exceed the range of recommended because over heat input might decrease the impact value.
3.Keep the arc as short as possible.
4.Take the back-step method at the arc starting to prevent blowholes.
5.Preheat the workpiece at 250-350°C and proceed PWHT.
Classificazione:
AWS A5.5 E9016-B91
Posizione di saldatura:
Composizione chimica tipica del metallo saldato (wt%)
| C | Mn | Si | P | S | Cr | Mo | Nb | V | W |
| 0.085 | 0.7 | 0.25 | 0.01 | 0.009 | 9.0 | 1.00 | 0.04 | 0.20 | 0.05 |
Proprietà meccaniche tipiche del metallo saldato
| YP N/mm² | TS N/mm² | EL % | PWHT |
| 655 | 789 | 20 | 740°C x1hr |
Dimensioni e intervallo di corrente consigliato (CA o CC+)
| Diametro (mm) | 3.2 | 4.0 | 5.0 | |
| Lunghezza (mm) | 350 | 450 | 450 | |
| Ampere | F | 80-130 | 100-180 | 160-210 |
| V&OH | 70-110 | 80-130 | – | |
| Peso per confezione (kg) | 5 | 5 | 5 | |
| Peso per cartone (kg) | 20 | 20 | 20 | |