Descrizione
Caratteristiche:
LSF-56 is a neutral flux. It is designed for butt or fillet submerged arc welding in combination with LSW-EH14.With nice bead appearance, good porosity resistance and good slag removability.
Applicazioni:
Typical applications include pressure vessels, shipbuilding, boilers and general steel structure.
Note sull'uso:
1. Dry the flux at 350℃ for 60 minutes before use.
2. Not recommended to welding more than two passes.
Classificazione:
AWS A5.17 F7A2-EH14
JIS Z3183 S502-H
Composizione chimica tipica del metallo saldato (wt%)
| C | Mn | Si | P | S |
| 0.08 | 1.72 | 0.24 | 0.011 | 0.011 |
Proprietà meccaniche tipiche del metallo saldato
| YP N/mm2 | TS N/mm2 | EL % | IV -40ºC J |
| 490 | 585 | 30 | 48 |
Dimensioni e range di corrente consigliato ( DC+)
| Filo: Diametro (mm) | 2.4 | 3.2 | 4.0 |
| Filo: Peso per rotolo (kg) | 25 | 25 | 25 |
| Flusso: Peso per sacco (kg) | 25 | 25 | 25 |