الوصف
الخصائص:
LKE-410 is used to give a martensitic weld metal of 13%Cr type for welding and building up of ferritic-martensitic steels. With good oxidization and corrosion resistance.
التطبيقات:
It is suitable for welding of the AISI 410 and AISI 420.Typical applications include constructions exposed to aggressive sulphuric gases in refineries, oil and gas industries and chemical plants.
ملاحظات حول الاستخدام:
1.Dry the electrodes at 250-300°C for 60 minutes and keep at 100-150°C before use.
2.Use lower currents and keep the arc as short as possible.
3.Preheat at 200-250°C, interpass temperature 180-250°C and post-weld heat treatment at 700-800°C
التصنيف:
AWS A5.4 E410-16
EN EN1600 E 13 R 1 2
JIS Z3221 D410-16
موضع اللحام:
التركيب الكيميائي النموذجي لمعدن اللحام (wt%)
| C | من | سي | P | S | كر | ني |
| 0.03 | 0.35 | 0.60 | 0.025 | 0.010 | 12.50 | 0.40 |
الخواص الميكانيكية النموذجية لمعدن اللحام
| TS N/mm² | EL % | PWHT |
| 540 | 24 | 750°C x1hr |
Sizes and recommended current range (AC or DC+)
| القطر (مم) | 2.6 | 3.2 | 4.0 | 4.8 | |
| الطول (مم) | 300 | 350 | 350 | 350 | |
| الأمبير | F | 60-90 | 80-130 | 130-170 | 180-210 |
| V&OH | 50-70 | 70-110 | 100-130 | – | |
| الوزن لكل عبوة (كجم) | 4/5 | 5 | 5 | 5 | |
| الوزن لكل كرتونة (كجم) | 20 | 20 | 20 | 20 | |