Descripción
Características:
LFC-701 is a flux cored wire suitable for flat and horizontal position welding. With excellent stable arc, low spatter, good slag detachability and deposition rate. It has good porosity resistance for fillet welding of zinc-primer coated steels.
Aplicaciones:
It is widely used for shipbuilding, bridge construction, offshore structure and general fabrication.
Notas sobre el uso:
1. Use DC(+) polarity.
2. Use CO₂ as shielding gas.
3. Proper preheat at range 50-150°C and maintain interpass temperature under 150°C.
Clasificación:
AWS A5.20 E70T-1C
EN EN758 T 42 2 R C 3 H10
JIS Z3313 YFW-C50DM
Posición de soldadura:
Composición química típica del metal de soldadura (wt%)
| C | Mn | Si | P | S |
| 0.05 | 1.55 | 0.60 | 0.017 | 0.007 |
Propiedades mecánicas típicas del metal de soldadura
| YP N/mm2 | TS N/mm2 | EL % | IV J | |
| 550 | 595 | 27 | -20°C | -30°C |
| 90 | 70 | |||
Tamaños y rango de corriente recomendado ( DC+)
| Diámetro (mm) | 1.2 | 1.6 | ||
| Posición de soldadura | F | HF | F | HF |
| Tensión (voltios) | 25-35 | 25-38 | 25-35 | 28-38 |
| Corriente(Amp) | 150-300 | 180-300 | 220-400 | 270-400 |
| Saliente (mm) | 15-25 | 15-25 | 20-20 | 20-30 |
| Caudal(l/min) | 15-25 | 15-25 | 20-25 | 20-25 |
| Peso por bobina (kg) | 15 | 15 | ||