Descripción
Características:
The weld metal of LKE-307 is a full austenite structure that contains 4-5% of Mn. With resistant to impact wearing and hot cracking.
Aplicaciones:
It is suitable for welding of stainless cladding steel, high tensile steel and self-hardening alloy steels with poor weldability.
Notas sobre el uso:
1.Dry the electrodes at 200-250°C for 60 minutes and keep at 100-150°C before use.
2.Clean up the slag with stainless steel brush to prevent impurity.
3.Use small heat input to reduce dilution, prevent cracking and improve impact value.
4.Keep the arc as short as possible.
Clasificación:
AWS A5.4 E307-16
EN EN1600 E 18 9 MnMo R 1 2
JIS Z3221 D307-16
Welding position:
Composición química típica del metal de soldadura (wt%)
| C | Mn | Si | P | S | Cr | Ni | Mo |
| 0.06 | 4.20 | 0.50 | 0.035 | 0.01 | 19.20 | 9.5 | 1.0 |
Propiedades mecánicas típicas del metal de soldadura
| TS N/mm² | EL % |
| 600 | 42 |
Sizes and recommended current range (AC or DC+)
| Diámetro (mm) | 2.6 | 3.2 | 4.0 | 5.0 | |
| Length (mm) | 300 | 350 | 350 | 350 | |
| Amperios | F | 60-90 | 80-130 | 130-170 | 180-210 |
| V&OH | 50-70 | 70-110 | 100-130 | – | |
| Peso por envase (kg) | 4/5 | 5 | 5 | 5 | |
| Weight per carton (kg) | 20 | 20 | 20 | 20 | |