Descrizione
Caratteristiche:
The weld metal of LKE-316L is a 18%Cr-12%Ni-2%Mo.It possesses properties to LKE-316 except with a much lower carbon content which reduces susceptibility to sensitization during welding.
Applicazioni:
It is suitable for welding of AISI 316,316L and cladding stainless steel.
Note sull'uso:
1.Dry the electrodes at 200-250°C for 60 minutes and keep at 100-150°C before use.
2.Use lower currents and keep the arc as short as possible.
Classificazione:
AWS A5.4 E316L-15
Posizione di saldatura:
Composizione chimica tipica del metallo saldato (wt%)
| C | Mn | Si | P | S | Cr | Ni | Mo |
| 0.03 | 1.20 | 0.35 | 0.016 | 0.010 | 19.50 | 13.20 | 2.50 |
Proprietà meccaniche tipiche del metallo saldato
| TS N/mm² | EL % |
| 570 | 40 |
Dimensioni e intervallo di corrente consigliato (CA o CC+)
| Diametro (mm) | 2.0 | 2.6 | 3.2 | 4.0 | 5.0 | |
| Lunghezza (mm) | 250 | 300 | 350 | 350 | 350 | |
| Ampere | F | 30-55 | 50-85 | 80-120 | 100-150 | 140-180 |
| V&OH | 20-50 | 45-80 | 70-110 | 90-135 | – | |
| Peso per confezione (kg) | 4/5 | 4/5 | 5 | 5 | 5 | |
| Peso per cartone (kg) | 20 | 20 | 20 | 20 | 20 | |