Descrizione
Caratteristiche:
LKE-8018-C3 is an iron powder low hydrogen electrode for the welding of low temperature service steel in all positions. The weld metal contains 1.0%Ni. The welding can be done with good X-ray soundness, high deposition rate, and good impact value at -45°C.
Applicazioni:
It is suitable for the welding of LPG tanks.
Note sull'uso:
1.Dry the electrodes at 300-350°C for 60 minutes before use.
2.Do not exceed the proper range of current, otherwise the impact value will decrease.
3.Take the back-step method at the arc starting.
4.Keep the arc as short as possible.
Classificazione:
AWS A5.5 E8018-C3
EN EN499 E 46 4 1Ni B 3 2
JIS Z3241 DL5026-4A1
Posizione di saldatura:
Composizione chimica tipica del metallo saldato (wt%)
| C | Mn | Si | P | S | Ni |
| 0.070 | 0.90 | 0.62 | 0.013 | 0.012 | 1.02 |
Proprietà meccaniche tipiche del metallo saldato
| YP N/mm² | TS N/mm² | EL % | IV -45°C J |
| 470 | 560 | 29 | 118 |
Dimensioni e intervallo di corrente consigliato (CA o CC+)
| Diametro (mm) | 2.6 | 3.2 | 4.0 | 5.0 | |
| Lunghezza (mm) | 300 | 350 | 400 | 400 | |
| Ampere | F | 70-100 | 100-140 | 140-180 | 180-230 |
| V&OH | 60-90 | 90-130 | 120-160 | – | |
| Peso per confezione (kg) | 4/5 | 5 | 5 | 5 | |
| Peso per cartone (kg) | 20 | 20 | 20 | 20 | |