LKE-NiCrFe-2 is a low hydrogen type and nickel-based covered electrode. The welding can be done in all position with good X-ray soundness and good crack resistance. The weld metal provides excellent mechanical properties which can satisfy the requirements of API and ASME for LNG tanks.
Applicazioni:
It is suitable for welding of ASTM B163/166/167/168,Inconel600,cryogenic steels, martensitic to austenitic steels, dissimilar steels etc.
Note sull'uso:
1.Dry the electrode at 350-400°C for 30-60 minutes.
2. Utilizzare un amperaggio ridotto e mantenere l'arco il più breve possibile.
3.Keep the interpass at 150°C.
4.Take back-step method to prevent blowhole at arc starting.
Classificazione:
AWS A5.11 ENiCrFe-2
JIS Z3224 DNiCrFe-2
Posizione di saldatura:
Composizione chimica tipica del metallo saldato (wt%)
| C | Mn | Si | P | S | Cr | Ni | Nb | Fe | Mo |
| 0.08 | 1.90 | 0.40 | 0.009 | 0.008 | 14.20 | 68.00 | 1.76 | 9.20 | 2.40 |
Proprietà meccaniche tipiche del metallo saldato
| TS N/mm² | EL % | IV -196°C J |
| 595 | 43 | 72 |
Dimensioni e intervallo di corrente consigliato (CA o CC+)
| Diametro (mm) | 2.6 | 3.2 | 4.0 | |
| Lunghezza (mm) | 300 | 350 | 350 | |
| Ampere | F | 60-90 | 70-120 | 100-150 |
| V&OH | 55-80 | 65-110 | 80-130 | |
| Peso per confezione (kg) | 5 | 5 | 5 | |
| Peso per cartone (kg) | 20 | 20 | 20 | |