Descrizione
Caratteristiche:
LKE-NiCrFe-3 is a low hydrogen type covered electrode. The welding can be done in all position with good heat resistance, oxidizations resistance and good corrosion resistance. Good toughness can be obtained at low temperature.
Applicazioni:
It is suitable for welding of Inconel 600, dissimilar steels, heat-resistant steels including ASTM B163/166/167.168.
Note sull'uso:
1.Be sure to clean up the contamination on the plates.
2. Utilizzare un amperaggio ridotto e mantenere l'arco il più breve possibile.
3.Dry the electrode at 350-400°C for 30-60 minutes.
4.Take back-step method to prevent blowhole at arc starting.
Classificazione:
AWS A5.11 ENiCrFe-3
JIS Z3224 DNiCrFe-3
Posizione di saldatura:
Composizione chimica tipica del metallo saldato (wt%)
| C | Mn | Si | P | S | Cr | Ti | Nb | Fe | Co | Ni |
| 0.035 | 6.5 | 0.35 | 0.01 | 0.008 | 14.50 | 0.01 | 1.20 | 3.5 | 0.01 | 73.5 |
Proprietà meccaniche tipiche del metallo saldato
| TS N/mm² | EL % | IV -196°C J |
| 630 | 41 | 98 |
Dimensioni e intervallo di corrente consigliato (CA o CC+)
| Diametro (mm) | 2.6 | 3.2 | 4.0 | |
| Lunghezza (mm) | 300 | 350 | 350 | |
| Ampere | F | 60-90 | 70-115 | 95-145 |
| V&OH | 55-80 | 65-110 | 85-135 | |
| Peso per confezione (kg) | 5 | 5 | 5 | |
| Peso per cartone (kg) | 20 | 20 | 20 | |