The weld metal of LKE-309 contains more Cr, Ni than LKE-308. The microstructure containing suitable quantity of ferrite, gives it an excellent resistance to hot cracking. It is suitable for welding of dissimilar metals, hardening alloy steel and steel with poor weldability.
アプリケーション
It is suitable for welding of stainless steel piping in refineries and chemical plants.
使用上の注意
1. Dry the electrodes at 200-250oC for 60 minutes and keep at 100-150oC before use.
2. Use lower currents for dissimilar metals welding.
分類
AWS A5.4 E309-16
EN EN1600 E 23 12 R 1 2
JIS Z3221 D309-16
溶接の位置
典型的な溶接金属の化学成分 (wt%)
| C | ムン | Si | Cr | モ | ニー | S | W | フェ |
| 0.018 | 0.28 | 0.19 | 22.47 | 14 | 54.26 | 0.002 | 3.21 | 5.14 |
溶接金属の代表的な機械的性質
| TS N/mm² | EL % | IV -30°C J |
| 770 | 40 | 70 |
サイズと推奨電流範囲（ACまたはDC+)
| 直径 (mm) | 2.6 | 3.2 | 4.0 | 4.8 | |
| 長さ (mm) | 300 | 350 | 350 | 350 | |
| アンペア | F | 90-120 | 120-160 | 160-220 | 230-300 |
| V&OH | 70-110 | 80-120 | 110-150 | 230-300 | |
| パックあたりの重量(kg) | 5 | 5 | 5 | 5 | |
| カートンあたりの重量（kg） | 20 | 20 | 20 | 20 | |