Descrição
Caraterísticas:
LKE-7018-W1 is an electrode for the welding of 490N/mm² grade high tensile steel.With good atmospheric corrosion resistance, good X-ray soundness and good crack resistance.
Aplicações:
It is suitable for welding of high tensile steel such as ASTM A588, COR-TEN A,B and also SPA-H,SMA 490 steel.
Notas sobre a utilização:
1.Dry the electrodes at 350-400°C for 60 minutes before use.
2.Take the back-step method at the arc starting to prevent blowholes.
3. manter o arco o mais curto possível.
4.While applying in plate with high restraint (such as the plates is thicker than 25mm),preheat at 80-100°C is recommended.
5.Do not exceed the range of recommended because over heat input might decrease the impact value.
Classificação:
AWS A5.5 E7018-W1
JIS Z3214 DA5016G
Posição de soldadura:
Composição química típica do metal de solda (wt%)
| C | Mn | Si | P | S | Cu | Ni | Cr |
| 0.06 | 0.60 | 0.50 | 0.02 | 0.01 | 0.50 | 0.35 | 0.25 |
Propriedades mecânicas típicas do metal de solda
| YP N/mm² | TS N/mm² | EL % | IV -20°C J |
| 470 | 578 | 31 | 142 |
Tamanhos e gama de corrente recomendada (CA ou CC+)
| Diâmetro (mm) | 3.2 | 4.0 | 5.0 | |
| Comprimento (mm) | 350 | 450 | 450 | |
| Amperes | F | 100-140 | 140-180 | 180-230 |
| V&OH | 80-130 | 120-160 | – | |
| Peso por embalagem (kg) | 5 | 5 | 5 | |
| Peso por caixa (kg) | 20 | 20 | 20 | |