Descrição
Caraterísticas:
LKE-9016-G is a low hydrogen electrode for the welding of 620 N/mm² grade high tensile steel. With good mechanical property and X-ray test.
Aplicações:
It is suitable for welding of shipbuilding, machine fabrication, offshore structure, pressure vessel, high pressure pipe and base metals are forging cast iron, structural steel, steel pipe for heat transfer, pressure vessel, alloy steel, ASTM A202/486 Gr90/736 Gr3, etc..
Notas sobre a utilização:
1.Preheat at 80°C is sometime required according to base metal or its thickness.
2.Do not exceed the range of recommended because over heat input might decrease the impact value.
3. manter o arco o mais curto possível.
4.Take the back-step method at the arc starting to prevent blowholes.
Classificação:
AWS A5.5 E9016-G
EN EN757 E 55 3 Z B T 1 2
JIS Z 3212 D5816
Posição de soldadura:
Composição química típica do metal de solda (wt%)
| C | Mn | Si | P | S | Ni | Mo |
| 0.085 | 1.40 | 0.50 | 0.02 | 0.05 | 1.1 | 0.30 |
Propriedades mecânicas típicas do metal de solda
| YP N/mm² | TS N/mm² | EL % | IV -60℃ J | PWHT |
| 580 | 650 | 24 | 80 | 620°C x1hr |
Tamanhos e gama de corrente recomendada (CA ou CC+)
| Diâmetro (mm) | 3.2 | 4.0 | 5.0 | |
| Comprimento (mm) | 350 | 450 | 450 | |
| Amperes | F | 90-130 | 130-180 | 180-240 |
| V&OH | 80-120 | 110-160 | 150-200 | |
| Peso por embalagem (kg) | 5 | 5 | 5 | |
| Peso por caixa (kg) | 20 | 20 | 20 | |