Описание
Характеристики:
LFC-2209 is a flux cored wire designed to weld duplex stainless steel such as UNS S31803 (Alloy 2205).With excellent pitting corrosion, stress corrosion resistance and crack resistance.
Приложения:
It is suitable for welding of heat exchanger, chemical equipment, pumps, vessels and pipes processing chloride containing solutions.
Примечания по использованию:
1. Use 100% CO₂ shielding gas.
2. Trailer Shield is required to ensure the weld pool completely shield until solidification is complete and no porosity problem.
3. Follow the recommended welding parameter to achieve good sound welds.
4. To prevent the welding defects due to improper gas shielding, the welding place should have the proper protection from wind.
Классификация:
AWS A5.22 E2209T1-1
EN EN12073 T 22 9 3NL P C 2
JIS Z3323 TS2209-FC1
Положение при сварке:
Типичный химический состав металла сварного шва (wt%)
| C | Mn | Si | P | S | Cr | Ni | Mo | Cu | N |
| 0.029 | 0.85 | 0.68 | 0.025 | 0.009 | 22.57 | 8.36 | 3.2 | 0.08 | 0.16 |
Типичные механические свойства металла сварного шва
| TS Н/мм2 | EL % |
| 786 | 26 |
Типоразмеры и рекомендуемый диапазон тока (DC+)
| Диаметр (мм) | 1.2 | |||
| Положение при сварке | F, HF | H | V-UP | OH |
| Напряжение (вольт) | 24-33 | 25-29 | 24-28 | 25-29 |
| Ток (Ампер) | 130-220 | 140-180 | 130-160 | 150-180 |
| Выступ (мм) | 15-20 | 15-20 | 15-20 | 15-20 |
| Скорость потока (л/мин) | 20-25 | 20-25 | 20-25 | 20-25 |
| Вес одной катушки (кг) | 12.5 | |||