Descrizione
Caratteristiche:
LFC-316H is designed for 100% CO₂ gas and all-position welding. It performs with excellent slag removal, almost spatter-free and high intergranular corrosion resistance to pressure vessel and high temperature application.
Applicazioni:
It is suitable for welding 304H 308H 316H
Note sull'uso:
1. Use 100% CO₂ shielding gas.
2. Use DC(+) polarity.
3. Trailer Shield is required to ensure the weld pool completely shield until solidification is complete and no porosity problem.
4. To get enough penetration in the down hand welding position recommend maintaining a higher welding speed.
Classificazione:
AWS A5.22 E316HT1-1
Posizione di saldatura:
Composizione chimica tipica del metallo saldato (wt%)
| C | Mn | Si | P | S | Cr | Ni | Mo |
| 0.055 | 0.69 | 0.025 | 0.01 | 0.008 | 18.8 | 12.63 | 2.75 |
Proprietà meccaniche tipiche del metallo saldato
| TS N/mm² | EL % |
| 780 | 30 |
Dimensioni e range di corrente consigliato ( DC+)
| Diametro (mm) | 1.2 | |||
| Posizione di saldatura | F, HF | H | V-UP | OH |
| Tensione (Volt) | 24-33 | 25-29 | 24-28 | 25-29 |
| Corrente (Amp) | 130-220 | 140-180 | 130-160 | 150-180 |
| Sporgenza (mm) | 15-20 | 15-20 | 15-20 | 15-20 |
| Portata (l/min) | 20-25 | 20-25 | 20-25 | 20-25 |
| Peso per bobina (kg) | 12.5 | |||