Descrizione
Caratteristiche:
LKE-NiCrMo-4 is a nickel based low hydrogen type covered electrode which contains less C and Si to reduce carbide precipitation in grain boundary. The excellent heat resistance and corrosion resistance are obtained for chemical plant and FGD equipments
Applicazioni:
It is suitable for HASTELLOY C-276 and dissimilar metal welding.
Note sull'uso:
1. Asciugare l'elettrodo a 350-400℃. for 30-60 minutes before use.
2.Use small amperage and keep the arc as short as possible
Classificazione:
| AWS A5.11 : | ENiCrMo-4 |
| ASME SFA-5.11 : | ENiCrMo-4 |
| EN ISO 14172 : | E Ni 6276 |
| JIS Z 3224 : | DNiCrMo-4 |
Posizione di saldatura:
Composizione chimica tipica del metallo saldato (wt%)
| C | Mn | Si | P | S | Cr | Ni | Nb | Fe | Mo |
| 0.07 | 0.78 | 0.32 | 0.002 | 0.004 | 20.80 | 59.60 | 3.52 | 5.40 | 8.90 |
Proprietà meccaniche tipiche del metallo saldato
| YS N/mm2 | TS N/mm2 | EL % | IV -196oC J |
| 490 | 770 | 38 | 69 |
Dimensioni e range di corrente consigliato (DC+)
| Diametro (mm) | 2.6 | 3.2 | 4.0 | |
| Lunghezza (mm) | 300 | 350 | 350 | |
| Ampere | F | 65-90 | 70-115 | 95-145 |
| V&OH | 60-80 | 60-110 | 80-130 | |
| Peso per confezione (kg) | 5 | 5 | 5 | |
| Peso per cartone (kg) | 20 | 20 | 20 | |