Descrizione
Caratteristiche:
LKE-8018-B2 is an iron powder low hydrogen electrode. The weld metal contains 1.25%Cr-0.5%Mo that makes the electrodes more suitable at 550°C ,With the characters of quiet and stable arc, little spatter.
Applicazioni:
It is suitable for welding of piping steels (STPA22,23, A335-P11, P12), casting steels (A217-WC6), and forging steels (A182-F11,F12).
Note sull'uso:
1.Dry the electrodes at 350-400°C for 60 minutes before use.
2.Take the back-step method at the arc starting.
3.Keep the arc as short as possible.
Classificazione:
AWS A5.5 E8018-B2
EN EN1599 E CrMo1 B 3 2
JIS Z3223 DT2318
Posizione di saldatura:
Composizione chimica tipica del metallo saldato (wt%)
| C | Mn | Si | P | S | Cr | Mo |
| 0.080 | 0.80 | 0.60 | 0.012 | 0.010 | 1.40 | 0.54 |
Proprietà meccaniche tipiche del metallo saldato
| YP N/mm² | TS N/mm² | EL % | PWHT |
| 590 | 675 | 26 | 690°C x1hr |
Dimensioni e intervallo di corrente consigliato (CA o CC+)
| Diametro (mm) | 3.2 | 4.0 | 5.0 | |
| Lunghezza (mm) | 350 | 400 | 400 | |
| Ampere | F | 90-140 | 140-190 | 190-240 |
| V&OH | 80-120 | 120-160 | – | |
| Peso per confezione (kg) | 5 | 5 | 5 | |
| Peso per cartone (kg) | 20 | 20 | 20 | |