Descrizione
Caratteristiche:
LWH-M deposits the weld metal of high Mn austenite structure. The welded metal provides good machining properties, good resistance to surfacing abrasion accompanied by heavy impact and good toughness.
Applicazioni:
It is suitable for dipper teeth, hammer mill, crusher, and rail road. etc.
Note sull'uso:
1.Dry the electrodes at 300-400°C for 60 minutes before use.
2.Do not exceed the range of recommended because over heat input might decrease the impact value.
3.Keep the arc as short as possible.
4.Thick plate should be preheat at 50-100°C
Posizione di saldatura:
Composizione chimica tipica del metallo saldato (wt%)
| C | Mn | Si |
| 0.75 | 12.00 | 0.42 |
Proprietà meccaniche tipiche del metallo saldato
| Condition | Vicker (HV) | Rockwell (HRC) | Shore (HS) |
| Working Hardening | 300 | 30 | 42 |
Dimensioni e intervallo di corrente consigliato (CA o CC+)
| Diametro (mm) | 3.2 | 4.0 | 5.0 | |
| Lunghezza (mm) | 350 | 400 | 450 | |
| Ampere | F | 90-140 | 130-190 | 180-250 |
| V&OH | 80-130 | 100-160 | – | |
| Peso per confezione (kg) | 5 | 5 | 5 | |
| Peso per cartone (kg) | 20 | 20 | 20 | |