Descrição
Caraterísticas:
LKE-10018-G is a low hydrogen electrode for the welding of 690 N/mm2 grade high tensile steel. With excellent crack resistance, good mechanical property and bead appearance.
Aplicações:
It is suitable for build-up welding before hardfacing. Proper base metals are forging cast iron, structural steel(HT70), pressure vessel(ASTM A225 Gr.C), carbon steel plate for mechanical fabrication(S45C),SAE 1345, ect..
Notas sobre a utilização:
1.Dry the electrodes at 350-400 °c for 60 minutes and keep at 100-150 °c before use.
2.Preheat the plates at 100-150 °c is before welding.
3. manter o arco o mais curto possível.
4.Take the back-step method at the arc starting to prevent blowholes.
Classificação:
AWS A5.5 E10018-G
EN EN757 E 62 5 Mn2NiMo B 3 2
JIS Z3212 D7016
Posição de soldadura:
Composição química típica do metal de solda (wt%)
| C | Mn | Si | P | S | Ni | Mo | Cr | V |
| 0.080 | 1.30 | 0.60 | 0.012 | 0.011 | 1.85 | 0.30 | 0.01 | 0.008 |
Propriedades mecânicas típicas do metal de solda
| YP N/mm2 | TS N/mm2 | EL % | IV -50 ºC J |
| 668 | 745 | 22 | 60 |
Sizes and recommended current range (AC or DC℃<+>℃)
| Diâmetro (mm) | 3.2 | 4.0 | 5.0 | |
| Comprimento (mm) | 350 | 450 | 450 | |
| Amperes | F | 120-150 | 160-200 | 180-240 |
| V & OH | 105-125 | 130-150 | – | |
| Peso por embalagem (kg) | 5 | 5 | 5 | |
| Peso por caixa (kg) | 20 | 20 | 20 | |