描述
特性：
LKE-10018-G is a low hydrogen electrode for the welding of 690 N/mm2 grade high tensile steel. With excellent crack resistance, good mechanical property and bead appearance.
應用：
It is suitable for build-up welding before hardfacing. Proper base metals are forging cast iron, structural steel(HT70), pressure vessel(ASTM A225 Gr.C), carbon steel plate for mechanical fabrication(S45C),SAE 1345, ect..
使用注意事項：
1.Dry the electrodes at 350-400 °c for 60 minutes and keep at 100-150 °c before use.
2.Preheat the plates at 100-150 °c is before welding.
3.Keep the arc as short as possible.
4.Take the back-step method at the arc starting to prevent blowholes.
分類：
AWS A5.5 E10018-G
EN EN757 E 62 5 Mn2NiMo B 3 2
JIS Z3212 D7016
焊接位置：
焊接金屬的典型化學成分 (wt%)
| C | 錳 | Si | P | S | 倪 | Mo | Cr | V |
| 0.080 | 1.30 | 0.60 | 0.012 | 0.011 | 1.85 | 0.30 | 0.01 | 0.008 |
焊接金屬的典型機械特性
| YP N/mm2 | TS N/mm2 | EL % | IV -50 ºC J |
| 668 | 745 | 22 | 60 |
Sizes and recommended current range (AC or DC℃<+>℃)
| 直徑 (mm) | 3.2 | 4.0 | 5.0 | |
| 長度 (mm) | 350 | 450 | 450 | |
| 安培數 | F | 120-150 | 160-200 | 180-240 |
| V & OH | 105-125 | 130-150 | – | |
| Weight per pack(kg) | 5 | 5 | 5 | |
| 每箱重量（公斤） | 20 | 20 | 20 | |