Caraterísticas:
Rutile-basic coated electrode for welding of creep resistant CrNi-alloyed austenitic stainless steels such as 304H. Controlled ferrite content of 3 – 8 FN. The deposit is resistant to embrittlement and scaling. Service temperatures up to 700ºC. Excellent weldability in all positions except vertical down.
Aplicações:
It is suitable for welding stainless 304H and service temperatures up to 700ºC.
Notas sobre a utilização:
1.Preheating normally not necessary.
2.Material with a thickness exceeding 25 mm is preferably preheated up to 150ºC.
3.Interpass temperature should not exceed 200ºC. Re-drying at 120 – 200ºC for min. 2 h if necessary.
Classificação:
AWS A5.4 E308H-16
EN EN 3581-A: E 19 9 H R
JIS Z3221 ES308H-16
Posição de soldadura:
Composição química típica do metal de solda (wt%)
| C | Mn | Si | P | S | Cr | Ni |
| 0.05 | 0.8 | 0.6 | 0.014 | 0.008 | 19.8 | 10.2 |
Propriedades mecânicas típicas do metal de solda
| TS N/mm² | EL % |
| 580 | 40 |
Tamanhos e gama de corrente recomendada (CA ou CC+)
| Diâmetro (mm) | 2.6 | 3.2 | 4.0 | |
| Comprimento (mm) | 300 | 350 | 350 | |
| Amperes | F | 45-75 | 70-110 | 110-145 |
| V&OH | 40-70 | 65-100 | 100-140 | |
| Peso por embalagem (kg) | 4/5 | 5 | 5 | |
| Peso por caixa (kg) | 20 | 20 | 20 | |