LKE-8016-G is a low hydrogen electrode for the welding of 550 N/mm² grade high tensile steel. With good strength property of deposited weld metal, slag removal, bead appearance and excellent weldability.
التطبيقات:
It is suitable for welding of high carbon steel, low manganese steels, ships, high pressure vessels,
pressure pipe and base metal ASTM A299/302/372, etc.
ملاحظات حول الاستخدام:
1.Dry the electrodes at 350-400℃ for 60 minutes before use.
2.Do not exceed the range of recommended because over heat input might decrease the impact value.
3- اجعل القوس قصيرًا قدر الإمكان.
4.Take the back-step method at the arc starting to prevent blowholes.
CLASSIFICATION
AWS A5.5 E8016-G
EN EN499 E 46 A Z B 1 2
JIS Z3212 D5316
موضع اللحام:
التركيب الكيميائي النموذجي لمعدن اللحام (wt%)
| C | من | سي | P | S |
| 0.080 | 1.5 | 0.60 | 0.014 | 0.010 |
الخواص الميكانيكية النموذجية لمعدن اللحام
| Yield strength MPa(ksi) | Tensile strength MPa(ksi) | Elongation % | Charpy V-Notch (J) | Post Weld Heat Treatment |
| 480 | 600 | 30 | 49 | 620 ºC x1hr |
الأحجام ونطاق التيار الموصى به (تيار متردد أو تيار مستمر ℃<++ ℃)
| القطر (مم) | 3.2 | 4.0 | 5.0 | |
| الطول (مم) | 350 | 450 | 450 | |
| الأمبير | F | 90-130 | 130-180 | 180-240 |
| V&OH | 80-120 | 110-160 | 150-200 | |
| الوزن لكل عبوة (كجم) | 5 | 5 | 5 | |
| الوزن لكل كرتونة (كجم) | 20 | 20 | 20 | |