描述
特性：
LKE-8016-G is a low hydrogen electrode for the welding of 550 N/mm² grade high tensile steel. With good strength property of deposited weld metal, slag removal, bead appearance and excellent weldability.
應用：
It is suitable for welding of high carbon steel, low manganese steels, ships, high pressure vessels,
pressure pipe and base metal ASTM A299/302/372, etc.
使用注意事項：
1.Dry the electrodes at 350-400℃ for 60 minutes before use.
2.Do not exceed the range of recommended because over heat input might decrease the impact value.
3.Keep the arc as short as possible.
4.Take the back-step method at the arc starting to prevent blowholes.
分類
AWS A5.5 E8016-G
EN EN499 E 46 A Z B 1 2
JIS Z3212 D5316
焊接位置：
焊接金屬的典型化學成分 (wt%)
| C | 錳 | Si | P | S |
| 0.080 | 1.5 | 0.60 | 0.014 | 0.010 |
焊接金屬的典型機械特性
| Yield strength MPa(ksi) | Tensile strength MPa(ksi) | Elongation % | Charpy V-Notch (J) | Post Weld Heat Treatment |
| 480 | 600 | 30 | 49 | 620 ºC x1hr |
Sizes and recommended current range (AC or DC℃<+>℃)
| 直徑 (mm) | 3.2 | 4.0 | 5.0 | |
| 長度 (mm) | 350 | 450 | 450 | |
| 安培數 | F | 90-130 | 130-180 | 180-240 |
| V&OH | 80-120 | 110-160 | 150-200 | |
| Weight per pack(kg) | 5 | 5 | 5 | |
| 每箱重量（公斤） | 20 | 20 | 20 | |