Description
Caractéristiques :
LKE-8016-G is a low hydrogen electrode for the welding of 550 N/mm² grade high tensile steel. With good strength property of deposited weld metal, slag removal, bead appearance and excellent weldability.
Applications :
It is suitable for welding of high carbon steel, low manganese steels, ships, high pressure vessels,
pressure pipe and base metal ASTM A299/302/372, etc.
Notes sur l'utilisation :
1.Dry the electrodes at 350-400℃ for 60 minutes before use.
2.Do not exceed the range of recommended because over heat input might decrease the impact value.
3.Keep the arc as short as possible.
4.Take the back-step method at the arc starting to prevent blowholes.
CLASSIFICATION
AWS A5.5 E8016-G
EN EN499 E 46 A Z B 1 2
JIS Z3212 D5316
Position de soudage :
Composition chimique typique du métal soudé (wt%)
| C | Mn | Si | P | S |
| 0.080 | 1.5 | 0.60 | 0.014 | 0.010 |
Propriétés mécaniques typiques du métal soudé
| Yield strength MPa(ksi) | Tensile strength MPa(ksi) | Elongation % | Charpy V-Notch (J) | Post Weld Heat Treatment |
| 480 | 600 | 30 | 49 | 620 ºC x1hr |
Sizes and recommended current range (AC or DC℃<+>℃)
| Diamètre (mm) | 3.2 | 4.0 | 5.0 | |
| Longueur (mm) | 350 | 450 | 450 | |
| Ampères | F | 90-130 | 130-180 | 180-240 |
| V&OH | 80-120 | 110-160 | 150-200 | |
| Poids par paquet (kg) | 5 | 5 | 5 | |
| Poids par carton (kg) | 20 | 20 | 20 | |