Description
Caractéristiques :
LSF-121T s designed for multi-pass groove welds. With nice bead appearance, porosity resistance and good slag removability. High welding efficiency, high toughness at low temperature can be obtained. It produces good impact property and minimum 500 N/mm² tensile strength when used with LSW-EG-F3
Applications :
Les applications typiques comprennent les appareils à pression, la construction navale et la structure générale en acier.
Notes sur l'utilisation :
1. Dry the flux at 350°C for 60 minutes before use.
2. When performing first pass welding, it is recommend to use lower current to prevent cracking.
Classification :
AWS A5.23 F9P8-EG-F3
Composition chimique typique du métal soudé (wt%)
| C | Mn | Si | P | S |
| 0.08 | 1.42 | 0.33 | 0.009 | 0.005 |
Propriétés mécaniques typiques du métal soudé
| YP N/mm2 | TS N/mm2 | EL % | IV -80ºC J |
| 550 | 650 | 23 | 55 |
Dimensions et plage de courant recommandée ( DC+)
| Fil : Diamètre (mm) | 2.4 | 3.2 | 4.0 |
| Fil : Poids par rouleau (kg) | 25 | 25 | 25 |
| Flux : Poids par sac (kg) | 25 | 25 | 25 |