LKE-8016-B8 is a low hydrogen electrode. The weld metal contains 9%Cr-1%Mo.With high tensile strength, good toughness and good heat resistance can be obtained.
アプリケーション
It is suitable for welding of 9%Cr-1%Mo steel such as ASTM A387 Gr.9 for refineries, petrochemical and electric power plants including pipe (ASTM A199-T9,A335-P9),drawing steel(A387-9),forging(A182-F9),etc.
使用上の注意
1.Dry the electrodes at 350-400°C for 60 minutes before use.
2.Do not exceed the range of recommended because over heat input might decrease the impact value.
3.Keep the arc as short as possible.
4.Take the back-step method at the arc starting to prevent blowholes.
5.Preheat the workpiece at 250-350°C and proceed PWHT.
分類
AWS A5.5 E8016-B8
EN EN1599 E CrMo9 B 1 2
JIS Z3223 DT2616
溶接の位置
典型的な溶接金属の化学成分 (wt%)
| C | ムン | Si | P | S | Cr | モ |
| 0.070 | 0.72 | 0.50 | 0.018 | 0.006 | 9.8 | 1.04 |
溶接金属の代表的な機械的性質
| YP N/mm² | TS N/mm² | EL % | PWHT |
| 600 | 715 | 23 | 740°C x1hr |
サイズと推奨電流範囲（ACまたはDC+)
| 直径 (mm) | 3.2 | 4.0 | 5.0 | |
| 長さ (mm) | 350 | 450 | 450 | |
| アンペア | F | 80-120 | 100-150 | 160-210 |
| V&OH | 70-110 | 80-130 | – | |
| パックあたりの重量（kg） | 5 | 5 | 5 | |
| カートンあたりの重量（kg） | 20 | 20 | 20 | |