Описание
Характеристики:
LKE-8016-B8 is a low hydrogen electrode. The weld metal contains 9%Cr-1%Mo.With high tensile strength, good toughness and good heat resistance can be obtained.
Приложения:
It is suitable for welding of 9%Cr-1%Mo steel such as ASTM A387 Gr.9 for refineries, petrochemical and electric power plants including pipe (ASTM A199-T9,A335-P9),drawing steel(A387-9),forging(A182-F9),etc.
Примечания по использованию:
1.Dry the electrodes at 350-400°C for 60 minutes before use.
2.Do not exceed the range of recommended because over heat input might decrease the impact value.
3.Keep the arc as short as possible.
4.Take the back-step method at the arc starting to prevent blowholes.
5.Preheat the workpiece at 250-350°C and proceed PWHT.
Классификация:
AWS A5.5 E8016-B8
EN EN1599 E CrMo9 B 1 2
JIS Z3223 DT2616
Положение для сварки:
Типичный химический состав металла сварного шва (wt%)
| C | Mn | Si | P | S | Cr | Mo |
| 0.070 | 0.72 | 0.50 | 0.018 | 0.006 | 9.8 | 1.04 |
Типичные механические свойства металла сварного шва
| YP N/mm² | TS N/mm² | EL % | PWHT |
| 600 | 715 | 23 | 740°C x1hr |
Sizes and recommended current range (AC or DC+)
| Диаметр (мм) | 3.2 | 4.0 | 5.0 | |
| Длина (мм) | 350 | 450 | 450 | |
| Амперы | F | 80-120 | 100-150 | 160-210 |
| V&OH | 70-110 | 80-130 | – | |
| Вес одной упаковки (кг) | 5 | 5 | 5 | |
| Вес в коробке (кг) | 20 | 20 | 20 | |