Caraterísticas:
LKE-8016-B8 is a low hydrogen electrode. The weld metal contains 9%Cr-1%Mo.With high tensile strength, good toughness and good heat resistance can be obtained.
Aplicações:
It is suitable for welding of 9%Cr-1%Mo steel such as ASTM A387 Gr.9 for refineries, petrochemical and electric power plants including pipe (ASTM A199-T9,A335-P9),drawing steel(A387-9),forging(A182-F9),etc.
Notas sobre a utilização:
1.Dry the electrodes at 350-400°C for 60 minutes before use.
2.Do not exceed the range of recommended because over heat input might decrease the impact value.
3. manter o arco o mais curto possível.
4.Take the back-step method at the arc starting to prevent blowholes.
5.Preheat the workpiece at 250-350°C and proceed PWHT.
Classificação:
AWS A5.5 E8016-B8
EN EN1599 E CrMo9 B 1 2
JIS Z3223 DT2616
Posição de soldadura:
Composição química típica do metal de solda (wt%)
| C | Mn | Si | P | S | Cr | Mo |
| 0.070 | 0.72 | 0.50 | 0.018 | 0.006 | 9.8 | 1.04 |
Propriedades mecânicas típicas do metal de solda
| YP N/mm² | TS N/mm² | EL % | PWHT |
| 600 | 715 | 23 | 740°C x1hr |
Tamanhos e gama de corrente recomendada (CA ou CC+)
| Diâmetro (mm) | 3.2 | 4.0 | 5.0 | |
| Comprimento (mm) | 350 | 450 | 450 | |
| Amperes | F | 80-120 | 100-150 | 160-210 |
| V&OH | 70-110 | 80-130 | – | |
| Peso por embalagem (kg) | 5 | 5 | 5 | |
| Peso por caixa (kg) | 20 | 20 | 20 | |