설명
특성:
LKE-9015-B92H4 is is designed to weld martensitic B9 (P92) alloyed steel: 9Cr steel to weld equivalent ‘type 92’ steels modified with tungsten, vanadium, niobium, nitrogen, and a small addition of boron to give improved long term creep properties
애플리케이션:
It is suitable for welding of Headers, Main steam piping, Turbine castings and Power generating plants
사용 시 참고 사항:
1.Preheat at 80°C is sometime required according to base metal or its thickness.
2.Do not exceed the range of recommended because over heat input might decrease the impact value.
3.Keep the arc as short as possible.
4.Take the back-step method at the arc starting to prevent blowholes.
분류:
AWS A5.5 E9015-B92H4
용접 위치:
용접 금속의 일반적인 화학 성분(wt%)
| C | Mn | Si | V | Cr | Ni | Mo | W |
| 0.11 | 0.60 | 0.25 | 0.21 | 9.00 | 0.60 | 0.45 | 1.70 |
용접 금속의 일반적인 기계적 특성
| YP N/mm² | TS N/mm² | EL % | IV -20°C J | PWHT |
| 620 | 740 | 22 | 50 | 620°C x1hr |
크기 및 권장 전류 범위(AC 또는 DC+)
| 지름(mm) | 3.2 | 4.0 | 5.0 | |
| 길이(mm) | 350 | 450 | 450 | |
| 앰프 | F | 90-130 | 130-180 | 180-240 |
| V&OH | 80-120 | 110-160 | 150-200 | |
| 팩당 무게(kg) | 5 | 5 | 5 | |
| 상자당 무게(kg) | 20 | 20 | 20 | |