Descrição
Caraterísticas:
LKE-9015-B92H4 is is designed to weld martensitic B9 (P92) alloyed steel: 9Cr steel to weld equivalent ‘type 92’ steels modified with tungsten, vanadium, niobium, nitrogen, and a small addition of boron to give improved long term creep properties
Aplicações:
It is suitable for welding of Headers, Main steam piping, Turbine castings and Power generating plants
Notas sobre a utilização:
1.Preheat at 80°C is sometime required according to base metal or its thickness.
2.Do not exceed the range of recommended because over heat input might decrease the impact value.
3. manter o arco o mais curto possível.
4.Take the back-step method at the arc starting to prevent blowholes.
Classificação:
AWS A5.5 E9015-B92H4
Posição de soldadura:
Composição química típica do metal de solda (wt%)
| C | Mn | Si | V | Cr | Ni | Mo | W |
| 0.11 | 0.60 | 0.25 | 0.21 | 9.00 | 0.60 | 0.45 | 1.70 |
Propriedades mecânicas típicas do metal de solda
| YP N/mm² | TS N/mm² | EL % | IV -20°C J | PWHT |
| 620 | 740 | 22 | 50 | 620°C x1hr |
Tamanhos e gama de corrente recomendada (CA ou CC+)
| Diâmetro (mm) | 3.2 | 4.0 | 5.0 | |
| Comprimento (mm) | 350 | 450 | 450 | |
| Amperes | F | 90-130 | 130-180 | 180-240 |
| V&OH | 80-120 | 110-160 | 150-200 | |
| Peso por embalagem (kg) | 5 | 5 | 5 | |
| Peso por caixa (kg) | 20 | 20 | 20 | |