特性：
LKE-9015-B92H4 is is designed to weld martensitic B9 (P92) alloyed steel: 9Cr steel to weld equivalent ‘type 92’ steels modified with tungsten, vanadium, niobium, nitrogen, and a small addition of boron to give improved long term creep properties
應用：
It is suitable for welding of Headers, Main steam piping, Turbine castings and Power generating plants
使用注意事項：
1.Preheat at 80°C is sometime required according to base metal or its thickness.
2.Do not exceed the range of recommended because over heat input might decrease the impact value.
3.Keep the arc as short as possible.
4.Take the back-step method at the arc starting to prevent blowholes.
分類：
AWS A5.5 E9015-B92H4
焊接位置：
焊接金屬的典型化學成分 (wt%)
| C | 錳 | Si | V | Cr | 倪 | Mo | W |
| 0.11 | 0.60 | 0.25 | 0.21 | 9.00 | 0.60 | 0.45 | 1.70 |
焊接金屬的典型機械特性
| YP N/mm² | TS N/mm² | EL % | IV -20°C J | PWHT |
| 620 | 740 | 22 | 50 | 620°C x1hr |
尺寸與建議電流範圍 (AC 或 DC+)
| 直徑 (mm) | 3.2 | 4.0 | 5.0 | |
| 長度 (mm) | 350 | 450 | 450 | |
| 安培數 | F | 90-130 | 130-180 | 180-240 |
| V&OH | 80-120 | 110-160 | 150-200 | |
| 每包重量（公斤） | 5 | 5 | 5 | |
| 每箱重量（公斤） | 20 | 20 | 20 | |