Description
Characteristics:
LKE-8012-C2 is an iron powder low hydrogen electrode for the welding of low temperature service steel. The weld metal contains 3.5%Ni. Good impact value can be obtained at -73°C. The welding can be done with good X-ray soundness, high deposition rate.
Applications:
It is suitable for the welding LPG tanks or 3.5%Ni steel for low temperature service.
Notes on Usage:
1.Dry the electrodes at 300-350°C for 60 minutes before use.
2.Do not exceed the proper range of current, otherwise impact value will decrease.
3.Take the back-step method at the arc starting.
4.Keep the arc as short as possible.
Classification:
AWS A5.5 E8018-C2
EN E499 E 46 6 3Ni B 3 2
JIS Z3241 DL5026-6P3
Welding position:
Typical chemical composition of weld metal (wt%)
| C | Mn | Si | P | S | Ni |
| 0.070 | 0.90 | 0.57 | 0.014 | 0.008 | 3.40 |
Typical mechanical properties of weld metal
| YP N/mm² | TS N/mm² | EL % | IV -73°C J | PWHT |
| 470 | 570 | 32 | 108 | 620°C x1hr |
Sizes and recommended current range (AC or DC+)
| Diameter (mm) | 2.6 | 3.2 | 4.0 | 5.0 | |
| Length (mm) | 300 | 350 | 400 | 400 | |
| Amps | F | 70-100 | 100-140 | 140-180 | 180-230 |
| V&OH | 60-90 | 90-130 | 120-160 | – | |
| Weight per pack (kg) | 4/5 | 5 | 5 | 5 | |
| Weight per carton (kg) | 20 | 20 | 20 | 20 | |